PA66 1300S

Leona™ 1300SPolyamide 66  General  datasheet
Material Status  •Commercial: Active
 
Literature 1  •Technical Datasheet (English)

 
Processing Method  •Injection Molding
 

Physical Dry Conditioned Unit Test Method
Specific Gravity 1.14 -- g/cm³ ASTM D792, ISO 1183
Molding Shrinkage - Flow  1.3 to 2.0 -- % Internal Method
Water Absorption        
Equilibrium -- 2.5 % ASTM D570
Equilibrium, 23°C, 50% RH -- 2.5 % ISO 62
Hardness Dry Conditioned Unit Test Method
Rockwell Hardness       ASTM D785, ISO 2039-2
M-Scale 80 55    
R-Scale 120 108    

Mechanical Dry Conditioned Unit Test Method
Tensile Modulus (23°C) 3000 1200 MPa ISO 527-2
Tensile Stress        
Yield, 23°C 82.0 52.0 MPa ISO 527-2
-- 79.0 57.0 MPa ASTM D638
Tensile Strain        
Yield, 23°C 4.0 24 % ISO 527-2
Break 50 250 % ASTM D638
Break, 23°C -- > 100 % ISO 527-2
Flexural Modulus        
-- 2800 1200 MPa ASTM D790
23°C 2700 1100 MPa ISO 178
Flexural Strength        
-- 118 54.0 MPa ASTM D790
23°C 113 42.0 MPa ISO 178
Taber Abrasion Resistance -- 7.00 mg ASTM D1044
Impact Dry Conditioned Unit Test Method
Charpy Notched Impact Strength 6.0 15 kJ/m² ISO 179
Charpy Unnotched Impact Strength No Break No Break   ISO 179
Notched Izod Impact 39 150 J/m ASTM D256

Thermal Dry Conditioned Unit Test Method
Deflection Temperature Under Load        
0.45 MPa, Unannealed 230 -- °C ASTM D648
0.45 MPa, Unannealed 192 -- °C ISO 75-2/B
1.8 MPa, Unannealed 70.0 -- °C ASTM D648
1.8 MPa, Unannealed 68.0 -- °C ISO 75-2/A
CLTE - Flow  0.000080 -- cm/cm/°C ASTM D696, ISO 11359-2
Specific Heat 1670 -- J/kg/°C No Standard
Thermal Conductivity 0.20 -- W/m/K No Standard

Electrical Dry Conditioned Unit Test Method
Surface Resistivity 1.0E+13 -- ohm IEC 60093
Volume Resistivity (23°C) 1.0E+14 -- ohm·cm IEC 60093
Electric Strength 20 -- kV/mm IEC 60243-1
Comparative Tracking Index (3.00 mm) 600 -- V IEC 60112
Flammability Dry Conditioned Unit Test Method
Flame Rating       UL 94
0.794 mm V-2 --    
1.59 mm V-2 --    

Injection Dry Unit  
Drying Temperature 80.0 to 90.0 °C  
Drying Time 2.0 to 3.0 hr  
Processing (Melt) Temp 270 to 290 °C  
Mold Temperature 75.0 to 85.0 °C