PA66 1300G

Physical Properties Metric English Comments
Density  1.22 g/cc 0.0441 lb/in³ ASTM D792
 
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate  100 MPa 14500 psi ASTM D638
Elongation at Break  2.0 % 2.0 % ASTM D638
Flexural Modulus  4.65 GPa 674 ksi ASTM D790
Izod Impact, Notched  0.430 J/cm
@Thickness 3.17 mm 0.806 ft-lb/in
@Thickness 0.125 in ASTM D256
 
Thermal Properties Metric English Comments
Melting Point  254 °C 489 °F ASTM D789
Deflection Temperature at 1.8 MPa (264 psi)  232 °C 450 °F ASTM D648
 
Processing Properties Metric English Comments
Rear Barrel Temperature  254 °C 490 °F 
Middle Barrel Temperature  268 °C 515 °F 
Front Barrel Temperature  285 °C 545 °F 
Nozzle Temperature  266 - 282 °C 510 - 540 °F 
Melt Temperature  271 - 293 °C 520 - 560 °F 
Mold Temperature  26.7 - 93.3 °C 80.0 - 200 °F 
Drying Temperature  71.1 °C 160 °F 
Dry Time  4 hour 4 hour 
Injection Pressure  68.9 MPa 10000 psi 
Back Pressure  0.0689 - 0.689 MPa 10.0 - 100 psi 
Screw Speed  30 - 60 rpm 30 - 60 rpm