Categories: Polymer; Thermoplastic; Cyclo Olefin Polymer
Material Notes: This grade is characterized by its high flowability and superior optical properties. It is suitable for optical components such as lenses and light guide panels where high molded precision is indispensable.
Information provided by Dongguan Yiding Plastic Raw Materials Co.,Ltd
Name: Richard Wang
Tel :0086 769 87190386
Mobile:0086 13662834186
Email:Richard_philips@163.com
Skype user: richwang16
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.010 % | 0.010 % | immersion @23°C; ISO 62 | ||
| Water Absorption at Saturation | 0.010 % | 0.010 % | |||
| Water Vapor Transmission | 0.0300 g/m²/day | 0.00193 g/100 in²/day | [g·mm/m2·d] @ 23°C and 85% RH; DIN 53122 | ||
| 0.250 g/m²/day | 0.0161 g/100 in²/day | Good barrier properties | |||
Melt Flow  |
26 g/10 min @Load 2.16 kg, Temperature 245 °C |
26 g/10 min @Load 4.76 lb, Temperature 473 °F |
ISO 1133 | ||
| 49 g/10 min @Load 2.16 kg, Temperature 260 °C |
49 g/10 min @Load 4.76 lb, Temperature 500 °F |
ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 46.0 MPa | 6670 psi | 5mm/min; ISO 527-1, 2 | ||
| Elongation at Break | 1.7 % | 1.7 % | 5mm/min; ISO 527-1, 2 | ||
| Tensile Modulus | 3.20 GPa | 464 ksi | 1mm/min; ISO 527-1, 2 | ||
| Charpy Impact Unnotched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.160 J/cm² | 0.761 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.2 @Frequency 1.00e+10 Hz |
2.2 @Frequency 1.00e+10 Hz |
|||
| Dissipation Factor | 0.00010 @Frequency 1.00e+10 Hz |
0.00010 @Frequency 1.00e+10 Hz |
|||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 241 °F | ISO 75-1, 2 | ||
| Glass Transition Temp, Tg | 140 °C | 284 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.53 | 1.53 | |||
| Transmission, Visible | 91 % | 91 % | ISO 13468-1 | ||
| Descriptive Properties | |||||
| Abbe number | 58 | ||||
| Birefringence, nm | max 20 | ||||
| Optical Stress Constant, Pa-1 | from -7E-12 to -2E-12 | ||||
| Pencil Hardness | F | JIS K5401 | |||
| Resistance to Acids | Usable | ||||
| Resistance to Alcohols | Usable | ||||
| Resistance to Alkalis | Usable | ||||
| Resistance to Aromatic Solvents | Not Usable | ||||
| Resistance to Chlorinated Solvents | Not Usable | ||||
| Resistance to Esters | Usable | ||||
| Resistance to Gasoline | Not Usable | ||||
| Resistance to Ketones | Usable | ||||
| Resistance to Oils | Not Usable | ||||