Material Notes: TOPAS® 5013S-04 is a high flow injection molding grade with a 130°C heat distortion temperature. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for healthcare and other high-tech products. This product features high flow characteristics for excellent mold detail replication. This grade has a high heat distortion temperature to withstand 121°C steam sterilization protocols, as well as gamma and EtO procedures.
Key applications and attributes:
•Drug delivery: Low leachables & extractables, low water transmission
•Bottles: Minimally reactive, EtO/gamma/steam sterilizable
•Surgical instruments: Chemically resistant to alcohol, acetone, and acrylates
•Labware: Temperature resistance, clarity and purity
•Optics: Clarity, low birefringence, low moisture sensitivity
•Electronics: Low dielectric constant, thermoplastic
•Healthcare and food: Broad regulatory approval
Information provided by Dongguan Yiding Plastic Raw Materials Co.,Ltd
Name: Richard Wang
Tel :0086 769 87190386
Mobile:0086 13662834186
Email:Richard_philips@163.com
Skype user: richwang16
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.010 % @Temperature 23.0 °C |
0.010 % @Temperature 73.4 °F |
ISO 62 |
| Melt Flow | 44 g/10 min @Load 2.16 kg, Temperature 260 °C |
44 g/10 min @Load 4.76 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Yield | 1.7 % | 1.7 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 3.20 GPa | 464 ksi | 1mm/min; ISO 527-2/1A |
| Charpy Impact Unnotched | 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.160 J/cm² @Temperature 23.0 °C |
0.761 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Dielectric Constant | 2.35 @Frequency 1000 - 10000 Hz |
2.35 @Frequency 1000 - 10000 Hz |
IEC 60250 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ISO 75-1,-2 |
| Vicat Softening Point | 135 °C | 275 °F | B50 (50°C/h 50N); ISO 306 |
| Glass Transition Temp, Tg | 134 °C | 273 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.53 | 1.53 | ISO 489 |
| Transmission, Visible | 91 % | 91 % | ISO 13468-2 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | <= 100 °C | <= 212 °F | |
| Nozzle Temperature | 240 - 300 °C | 464 - 572 °F | |
| Zone 1 | 230 - 260 °C | 446 - 500 °F | |
| Zone 2 | 240 - 270 °C | 464 - 518 °F | |
| Zone 3 | 250 - 280 °C | 482 - 536 °F | |
| Zone 4 | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 95.0 - 125 °C | 203 - 257 °F | |
| Injection Velocity | 50.0 - 150 mm/sec | 1.97 - 5.91 in/sec | Moderate to Fast |
| Injection Pressure | 50.0 - 110 MPa | 7250 - 16000 psi | Specific |
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | Specific |
| Back Pressure | <= 15.0 MPa | <= 2180 psi | Specific |
| Screw Speed | 50 - 200 rpm | 50 - 200 rpm | |