Material Notes: TOPAS® 6013F-04 is a high temperature, general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer and blended cast applications, and in coextrusion and blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging.
Key applications and attributes:
•Pharmaceutical blisters: Clarity, forming, barrier, purity, halogen-free
•Decorative film and sheet: Gloss, hardness, chemical resistance, forming
•Food packaging: Hot-fill, easy or linear tear, purity
•Healthcare and food: Broad regulatory approval
Information provided by Dongguan Yiding Plastic Raw Materials Co.,Ltd
Name: Richard Wang
Tel :0086 769 87190386
Mobile:0086 13662834186
Email:Richard_philips@163.com
Skype user: richwang16
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Oxygen Permeability | 1120 cm3 mil/(m2 day atm) | 72.26 cm3 mil/(100 in2 day atm) | |||
| Water Vapor Permeability | 6.20 g mil/ (m2 day) | 0.400 g mil/ (100 in2 day) | |||
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 | ||
| Water Absorption at Saturation | 0.010 % @Temperature 23.0 °C |
0.010 % @Temperature 73.4 °F |
ISO 62 | ||
| Water Vapor Transmission | 0.000130 g/m²/day @Temperature 38.0 °C |
0.00000837 g/100 in²/day @Temperature 100 °F |
90% RH; ISO 15106-3 | ||
| Oxygen Transmission | 28.0 cc-mm/m²-24hr-atm @Temperature 23.0 °C |
71.1 cc-mil/100 in²-24hr-atm @Temperature 73.4 °F |
50% RH; ASTM D3985 | ||
| Thickness | 70.0 microns | 2.76 mil | Film | ||
| Melt Flow | 0.92 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.92 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 2.4 % | 2.4 % | ISO 527-3 | ||
| Film Elongation at Break, TD | 2.2 % | 2.2 % | ISO 527-3 | ||
| Tensile Modulus | 2.25 GPa | 326 ksi | Film, TD; ISO 527-3 | ||
| 2.40 GPa | 348 ksi | Film, MD; ISO 527-3 | |||
| Elmendorf Tear Strength MD | 9.0 g | 9.0 g | ISO 6383-2 | ||
| Elmendorf Tear Strength TD | 9.0 g | 9.0 g | ISO 6383-2 | ||
| Dart Drop Test | <= 36.0 g | <= 0.0794 lb | F50; ISO 7765-1 | ||
| Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ISO 527-3 | ||
| Film Tensile Strength at Break, TD | 45.0 MPa | 6530 psi | ISO 527-3 | ||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | 138 °C | 280 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | <= 1.0 % | <= 1.0 % | Film; ISO 14782 | ||
| Gloss | >= 100 % | >= 100 % | 60°, Film; ISO 2813 | ||
| Descriptive Properties | |||||
| Type of film extrusion | Cast | Test specimen | |||