Material Notes: TOPAS® 6013M-07 is an injection molding grade with a wide processing window, especially suited for blow molding processes including IBM and ISBM. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for healthcare and other high-tech products. Lower leachables and extractables of TOPAS COC preserve food and drug stability and quality. It is a non-polar substrate that does not promote adsorption, denaturation, aggregation, or precipitation like glass can. This grade has a high (130°C) heat distortion temperature to withstand 121°C steam sterilization protocols, as well as gamma and EtO procedures.
Key applications and attributes:
•Drug delivery: Low leachables & extractables, low water transmission
•Prefilled syringes, vials, cartridges: Non-ionic, does not promote adsorption like glass
•Bottles: Minimally reactive, EtO/gamma/steam sterilizable
•Surgical instruments: Chemically resistant to alcohol, acetone, and acrylates
•IV containers and components: Transparent, withstands EtO/gamma/steam sterilization
•Labware: Temperature resistance, clarity and purity
•Optics: Clarity, low birefringence, low moisture sensitivity
•Electronics: Low dielectric constant, thermoplastic
•Healthcare and food: Broad regulatory approval
Information provided by Dongguan Yiding Plastic Raw Materials Co.,Ltd
Name: Richard Wang
Tel :0086 769 87190386
Mobile:0086 13662834186
Email:Richard_philips@163.com
Skype user: richwang16
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.010 % @Temperature 23.0 °C |
0.010 % @Temperature 73.4 °F |
ISO 62 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 260 °C |
12 g/10 min @Load 4.76 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Stress | 63.0 MPa | 9140 psi | Break, (5mm/min); ISO 527-2,-1A |
| Elongation at Yield | 2.6 % | 2.6 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 2.90 GPa | 421 ksi | 1mm/min; ISO 527-2/1A |
| Charpy Impact Unnotched | 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.170 J/cm² @Temperature 23.0 °C |
0.809 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75-1,-2 |
| Glass Transition Temp, Tg | 142 °C | 288 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.53 | 1.53 | ISO 489 |
| Transmission, Visible | 91 % | 91 % | ISO 13468-2 |