Material Notes: TOPAS® 8007D-61 is an externally lubricated version of our 8007 series of injection molding resins, targeting injection blow molding (IBM) and injection stretch blow molding (ISBM) applications. Like the rest of the 8007 series, 8007D-61 is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for healthcare and food products. Lower leachables and extractables of TOPAS COC preserve food and drug stability and quality.
Key applications and attributes:
•Drug delivery: Low leachables & extractables, low water transmission
•Prefilled syringes, vials, cartridges: Non-ionic, does not promote adsorption like glass
•Bottles and tubes: Minimally reactive, EtO and irradiation sterilizable
•Surgical instruments: Chemically resistant to alcohol, acetone, and acrylates
•IV containers and components: Transparent, withstands EtO and gamma sterilization
•Labware: Temperature resistance, clarity and purity
•Food packaging: Not manufactured with BPA, phthalates, or halogens
•Healthcare and food: Broad regulatory approval
Information provided by Dongguan Yiding Plastic Raw Materials Co.,Ltd
Name: Richard Wang
Tel :0086 769 87190386
Mobile:0086 13662834186
Email:Richard_philips@163.com
Skype user: richwang16
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Permeability | 0.985 g mil/ (m2 day) | 0.0635 g mil/ (100 in2 day) | |
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.010 % @Temperature 23.0 °C |
0.010 % @Temperature 73.4 °F |
ISO 62 |
| Water Vapor Transmission | 0.0000250 g/m²/day @Temperature 23.0 °C |
0.00000161 g/100 in²/day @Temperature 73.4 °F |
85% RH; DIN 53122 |
| Melt Flow | 29.4 g/10 min @Load 2.16 kg, Temperature 260 °C |
29.4 g/10 min @Load 4.76 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Yield | 4.5 % | 4.5 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1mm/min; ISO 527-2/1A |
| Charpy Impact Unnotched | 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.260 J/cm² @Temperature 23.0 °C |
1.24 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Dielectric Constant | 2.35 @Frequency 1000 - 10000 Hz |
2.35 @Frequency 1000 - 10000 Hz |
IEC 60250 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ISO 75-1,-2 |
| Vicat Softening Point | 80.0 °C | 176 °F | B50 (50°C/h 50N); ISO 306 |
| Glass Transition Temp, Tg | 78.0 °C | 172 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.53 | 1.53 | ISO 489 |
| Transmission, Visible | 91 % | 91 % | ISO 13468-2 |