Material Notes: TOPAS® 8007X10 is a highly UV-transparent version of our 8007 series of injection molding resins. Like the rest of the 8007 grades, 8007X10 is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for diagnostic and analytical products. It transmits ultraviolet light at lower wavelengths than other polymers. Analytical results are more accurate with pure TOPAS COC and its higher UV transmission for more precise analysis in contact with sensitive chemistries.
Key applications and attributes:
•Cuvettes: UV transparency at low wavelengths
•Microplates and biochips: Dimensional stability and purity and chemical resistance
•Microfluidics: UV transmission; exceptional mold detail replication
•Optics: Clarity, low birefringence, low fluorescence
•High purity applications: Not manufactured with BPA, phthalates, or halogens
Information provided by Dongguan Yiding Plastic Raw Materials Co.,Ltd
Name: Richard Wang
Tel :0086 769 87190386
Mobile:0086 13662834186
Email:Richard_philips@163.com
Skype user: richwang16
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.010 % @Temperature 23.0 °C |
0.010 % @Temperature 73.4 °F |
ISO 62 |
| Melt Flow | 29.4 g/10 min @Load 2.16 kg, Temperature 260 °C |
29.4 g/10 min @Load 4.76 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50mm/min; ISO 527-2/1A |
| Elongation at Yield | 4.5 % | 4.5 % | 50mm/min; ISO 527-2/1A |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1mm/min; ISO 527-2/1A |
| Charpy Impact Unnotched | 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.260 J/cm² @Temperature 23.0 °C |
1.24 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Dielectric Constant | 2.35 @Frequency 1000 - 10000 Hz |
2.35 @Frequency 1000 - 10000 Hz |
IEC 60250 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ISO 75-1,-2 |
| Vicat Softening Point | 80.0 °C | 176 °F | B50 (50°C/h 50N); ISO 306 |
| Glass Transition Temp, Tg | 78.0 °C | 172 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.53 | 1.53 | ISO 489 |
| Transmission, Visible | 91 % | 91 % | ISO 13468-2 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | <= 60.0 °C | <= 140 °F | |
| Nozzle Temperature | 220 - 250 °C | 428 - 482 °F | |
| Zone 1 | 190 - 220 °C | 374 - 428 °F | |
| Zone 2 | 200 - 230 °C | 392 - 446 °F | |
| Zone 3 | 210 - 240 °C | 410 - 464 °F | |
| Zone 4 | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | |
| Injection Velocity | 50.0 - 150 mm/sec | 1.97 - 5.91 in/sec | Moderate to Fast |
| Injection Pressure | 50.0 - 110 MPa | 7250 - 16000 psi | Specific |
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | Specific |
| Back Pressure | <= 15.0 MPa | <= 2180 psi | Specific |
| Screw Speed | 50 - 200 rpm | 50 - 200 rpm | |