Material Notes: TOPAS® 9506F-500 is a high clarity extrusion grade for use in shrink, food and medical packaging as either a discrete layer in multilayer film or in blends with polyethylene. It is designed to deliver high shrinkage at low temperatures in shrink packaging applications. It has low glass transition temperature and provides excellent clarity, stiffness, water vapor barrier and good thermoformability.
Key applications and attributes:
•Shrink films and labels: High shrink at low temperatures, low stress, toughness
•Food packaging: Not manufactured with BPA, phthalates, or halogens
•Food contact: Broad regulatory approval
Information provided by Dongguan Yiding Plastic Raw Materials Co.,Ltd
Name: Richard Wang
Tel :0086 769 87190386
Mobile:0086 13662834186
Email:Richard_philips@163.com
Skype user: richwang16
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Oxygen Permeability | 775 cm3 mil/(m2 day atm) @Temperature 23.0 °C |
50.0 cm3 mil/(100 in2 day atm) @Temperature 73.4 °F |
50% RH; ASTM D3985 | ||
| Water Vapor Permeability | 4.60 g mil/ (m2 day) @Temperature 38.0 °C |
0.297 g mil/ (100 in2 day) @Temperature 100 °F |
90% RH; ISO 15106-3 | ||
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 | ||
| Water Absorption at Saturation | 0.010 % @Temperature 23.0 °C |
0.010 % @Temperature 73.4 °F |
ISO 62 | ||
| Thickness | 70.0 microns | 2.76 mil | Film | ||
Melt Flow  |
0.92 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.92 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| 5.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 2.9 % | 2.9 % | ISO 527-3 | ||
| Film Elongation at Break, TD | 3.6 % | 3.6 % | ISO 527-3 | ||
| Tensile Modulus | 1.70 GPa | 247 ksi | Film, MD; ISO 527-3 | ||
| 2.00 GPa | 290 ksi | Film, TD; ISO 527-3 | |||
| Elmendorf Tear Strength MD | 230 g | 230 g | ISO 6383-2 | ||
| Elmendorf Tear Strength TD | 240 g | 240 g | ISO 6383-2 | ||
| Dart Drop Test | <= 36.0 g | <= 0.0794 lb | F50; ISO 7765-1 | ||
| Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ISO 527-3 | ||
| Film Tensile Strength at Break, TD | 55.0 MPa | 7980 psi | ISO 527-3 | ||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | 65.0 °C | 149 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | >= 2.0 % | >= 2.0 % | Film; ISO 14782 | ||
| Gloss | >= 100 % | >= 100 % | 60°, Film; ISO 2813 | ||
| Descriptive Properties | |||||
| Type of film extrusion | Cast | Test specimen | |||